This study evaluated the effects of resin luting agents (LA) polymerized using increased temperature on the in vitro microtensile bond strength (mTBS) of indirect restorations to dentin. The occlusal dentin surfaces of 40 human third molars were exposed and flattened. The teeth were assigned to 8 groups (n = 5) according to the LA temperature (25°C o r 50°C), curing mode (dual- or self-curing mode), and product (Excite DSC/Variolink II [VII] and XP Bond/Calibra [Cal]). The bonding agents were applied to the dentin surfaces according to manufacturers' instructions. For preheated groups, the LAs were heated to 50°C, subsequently mixed on a heated stirrer surface, and applied to the previously heated pre-polymerized resin discs (2 mm thickness, TPH-Spectrum). The discs were bonded to the dentin surfaces, and the LAs were either exposed to a curing light according to manufacturers' instructions or allowed to self-cure. Specimens were stored in relative humidity at 37°C for 7 days. Specimens were mesio-distally and bucco-lingually sectioned to obtain multiple bonded beams with a 1-mm² cross-sectional area for mTBS testing. Data (MPa) were analyzed by 2-way ANOVA and Tukey's post hoc test (a = 5%) for each product. Specimen failure patterns were analyzed using a scanning electron microscope. VII groups showed higher mTBS at 50°C than at 25°C regardless of curing mode (p = 0.05). Cal groups showed similar mTBS at 25°C and 50°C in all activation modes. The use of some dual-polymerizing LAs at 50°C may improve the mTBS of indirect restorations to dentin.

OBJECTIVES: This study evaluated the effects of light exposure through simulated indirect ceramic restorations (SICR) on hardness (KHN) of dual-cured resin cements (RCs), immediately after light-activation and 24 h later. MATERIAL AND METHODS: Three dual-cured RCs were evaluated: Eco-Link (Ivoclar Vivadent), Rely X ARC (3M ESPE), and Panavia F (Kuraray Medical Inc.). The RCs were manipulated in accordance to the manufacturers' instructions and were placed into cylindrical acrylic matrixes (1-mm-thick and 4-mm diameter). The RC light-activation (Optilux 501; Demetron Kerr) was performed through a glass slide for 120 s (control group), or through 2-mm or 4-mm thick SICRs (IPS Empress II; Ivoclar Vivadent). The specimens were submitted to KHN analysis immediately and 24 h after light-activation. The data obtained at the 2 evaluation intervals were submitted to 2-way ANOVA repeated measures and post-hoc Tukey's test (pre-set alpha of 5%). RESULTS: Lower KHN was observed when light-activation was performed through SICRs for Eco-Link at all evaluation intervals and for Rely X ARC 24 h later. For Panavia F, no significant difference in KHN was observed between control and experimental groups, regardless of evaluation interval. Most groups exhibited higher KHN after 24 h than immediately after light-activation, with the exception of Rely X ARC light-activated through SICR, as no significant difference in KHN was found between evaluation intervals. CONCLUSIONS: Light overexposure did not compensate for light intensity attenuation due to the presence of SICR when Rely X and Eco-Link were used. Although hardness of such RCs increased over a 24-h interval, the RCs subjected to light overexposure did not reach the hardness values exhibited after direct light exposure.

This study evaluated the Knoop Hardness (KHN) values of two dual-cured composite resin core build-up materials and one resin cement exposed to different curing conditions. Two dual-cured core build-up composite resins (LuxaCore®-Dual, DMG; and FluoroCore®2, Dentsply Caulk), and one dual-cured resin cement (Rely X ARC, 3M ESPE) were used in the present study. The composite materials were placed into a cylindrical matrix (2 mm in height and 3 mm in diameter), and the specimens thus produced were either light-activated for 40 s (Optilux 501, Demetron Kerr) or were allowed to self-cure for 10 min in the dark (n = 5). All specimens were then stored in humidity at 37°C for 24 h in the dark and were subjected to KHN analysis. The results were submitted to 2-way ANOVA and Tukey's post-hoc test at a pre-set alpha of 5%. All the light-activated groups exhibited higher KHN values than the self-cured ones (p = 0.00001), regardless of product. Among the self-cured groups, both composite resin core build-up materials showed higher KHN values than the dual-cured resin cement (p = 0.00001). LuxaCore®-Dual exhibited higher KHN values than FluoroCore®2 (p = 0.00001) when they were allowed to self-cure, while no significant differences in KHN values were observed among the light-activated products. The results suggest that dual-cured composite resin core build-up materials may be more reliable than dual-cured resin cements when curing light is not available.